Products
F332
Injection Molding Grade
Melting rate(220°C,10kg)
16g/10min
Vicat softening temperature B50
102°C
Notched impact strength of cantilever beam
19kJ/㎡
Gloss
80，@60°
Feature
Excellent glossiness
Medium to high heat resistance
Moderate shocks
Medium to high heat resistance
Moderate shocks
C442
Injection molding/extrusion molding grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
105℃
Notched impact strength of cantilever beam
16kJ/㎡
Gloss
75，@60°
Feature
high heat resistance
High Impact
High Impact
L322
Injection Molding Grade
Melting rate(220°C,10kg)
26 g/10min
Vicat softening temperature B50
98°C
Notched impact strength of cantilever beam
20kJ/㎡
Gloss
93，@60°
Feature
Excellent liquidity
Excellent glossiness
Moderate shocks
Excellent glossiness
Moderate shocks
B432/E
Injection molding/extrusion molding grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
102℃
Notched impact strength of cantilever beam
19kJ/㎡
Gloss
60，@60°
Feature
Medium to high heat resistance
High stretch ratio
Good surface smoothness
High stretch ratio
Good surface smoothness
B732/E
Injection molding/extrusion molding grade
Melting rate(220°C,10kg)
7 g/10min
Vicat softening temperature B50
103℃
Notched impact strength of cantilever beam
25kJ/㎡
Gloss
75，@60°
Feature
High Impact
Medium to high heat resistance
Medium to high heat resistance
M4
Injection molding/extrusion molding grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
101℃
Notched impact strength of cantilever beam
10kJ/㎡
Gloss
10，@60°
Feature
matte
High stretch ratio
Smooth surface finish
High stretch ratio
Smooth surface finish
02 Technical advantages