Products
F332
Injection grade
Melting rate(220°C,10kg)
16g/10min
Vicat softening temperature B50
102°C
Notched impact strength of cantilever beam
19kJ/㎡
Gloss
2350MPa
Feature
Excellent comprehensive performance balance
Medium to high heat resistance, balancing impact and melt index
Medium to high heat resistance, balancing impact and melt index
C442
Injection grade/extrusion grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
105℃
Notched impact strength of cantilever beam
16kJ/㎡
Gloss
2350MPa
Feature
high heat resistance
Moderate impact
Moderate melting point
Moderate impact
Moderate melting point
L322
Injection grade
Melting rate(220°C,10kg)
26 g/10min
Vicat softening temperature B50
98°C
Notched impact strength of cantilever beam
20kJ/㎡
Gloss
93GU
Feature
high gloss
High liquidity
High liquidity
B432/E
Extrusion grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
102℃
Notched impact strength of cantilever beam
19kJ/㎡
Gloss
60GU
Feature
Medium to high heat resistance
High stretch ratio
low gloss
High stretch ratio
low gloss
B732/E
Extrusion grade
Melting rate(220°C,10kg)
7 g/10min
Vicat softening temperature B50
103℃
Notched impact strength of cantilever beam
25kJ/㎡
Gloss
2300MPa
Feature
High-impact
Medium to high heat resistance
Medium to high heat resistance
M4
Extrusion grade
Melting rate(220°C,10kg)
9 g/10min
Vicat softening temperature B50
101℃
Notched impact strength of cantilever beam
10kJ/㎡
Gloss
10GU
Feature
Ultra matte finish
High stretch ratio
Smooth surface finish
High stretch ratio
Smooth surface finish
02 Technical advantages